Co2+:MgAl2O4 ( Co2+:Spinel) Crystals Co Spinel Passive Q Switches
Co2+:MgAl2O4 (Co2+:Spinel or Co:MALO) crystals is a new material
for passive Q-switching in lasers emitting from 1.2 to 1.6 µm, in
particular, for eye-safe 1.54 µm Er:glass laser, but also works at
1.44 µm and 1.34 µm wavelengths.
High absorption cross section (3.5 × 10-19cm2) permits Q-switching
of Er:glass laser without intracavity focusing both with flash-lamp
and diode-laser pumping.
Negligible excited-state absorption results in high contrast of
Q-switch, i.e. the ratio of initial (small signal) to saturated
absorption is higher than 10.
We offer the high quality Co:Spinel crystals materials with high
optical quality and uniform distribution of Co2+ in laser grade
polishing and coatings.
| Specifications | |
| Material | Co2+:MgAl2O4 |
| Orentation | <111>+/-0.5° |
| Doping rate of Co2+ | 0.05-0.3 atm% |
| Optical density | 0.1-0.9 |
| Absorption coefficient | 1.0cm-1-7cm-1 |
| Transmittance | 30%-99% |
| Absorption section | 3.5 x 10-19cm2 |
| Thickness/Diameter tolerance | +/-0.1mm |
| Parallelism | 10″ |
| Perpendicular | 5′ |
| Surface quality | 10/5 |
| Wavefront distortion | Lambda/8 @ 632nm |
| Flatness | Lambda/8 @ 632nm |
| Aperture | >90% |
| Chamfer | 0.1 x 45° |
| HR Coating | <=0.2%(@ 1533nm) |
| Damage threshold | >500MW/cm2 |
About US
Crystro has perfect automatic production equipment, the current products are mainly concentrated in the YAG, TGG, TSAG,GGG, LGS, Ce:GAGG , Ce:YAG andCe: LuYAG production. the application of advanced process technology of manufacturing, reducing energy consumption to ensure sustainable development field of research and development.
|
|